 L (C. 0.35), when treated by the uniform method usually adopted for chain-cable irons, made the worst welds. Iron K, with carbon so low as 0.07, made bad welds, although it was otherwise a good average chainiron, with a medium amount of impurity. Carbon,...  Report of the United States Board Appointed to Test Iron, Steel and Other ... - Page 235by United States. Board for Testing Iron, Steel, and Other Metals - 1881Full view - About this book
 | United States. Board for testing iron, steel and other metals - Metals - 1878 - 862 pages
...0.042, 0.055, 0.033, 0.032, 0.0044, 0.08, and, including L, 0.351. The weld-steel, or steely iron, L (C. 0.035), when treated by the uniform method usually...temperatures of low-carbon irons. Slag was highest (2.2G per cent.) in the 2-inch bar of iron tf, which welded less soundly than any other bar of the... | |
 | United States. Board for testing iron, steel and other metals - Metals - 1878 - 842 pages
...0.033, 0.032, 0.0044, 0.08, and, including L, 0.331. The weld-steel, or steely iron, L (С. 0.033), when treated by the uniform method usually adopted...temperatures of low-carbon irons. Slag was highest (2.26 per ceut.) in the 2-inch bar of iroii N, which welded less soundly than any other bar of the... | |
 | Board for Testing Iron, Steel and Other Metals - 1878 - 318 pages
...0.042, 0.055, 0.033, 0.032, 0.0044, 0.68, and, including L, 0.351. The weld-steel, or steely iron, L (C. 0.035), when treated by the uniform method usually...than phosphorus, promotes fluidity, hence the iron is u burned " at the ordinary welding temperatures of low-carbon irons. Slag was highest (2.2G per cent.)... | |
 | Lester Anthony Beardslee - Chains - 1879 - 142 pages
...0.055, 0.033, 0.032, 0.044, 0.068, and including L, 0.351. The weld steel, or steely iron, L (C. 0.35), when treated by the uniform method usually adopted...temperatures of low-carbon irons. Slag was highest (2.26 per cent) in the two-inch bar of iron N, which welded less soundly than any other bar of the... | |
 | Lester Anthony Beardslee - Chains - 1879 - 142 pages
...0.055, 0.033, 0.032, 0.044, 0.068, and including L, 0.351. The weld steel, or steely iron, L (C. 0.35), when treated by the uniform method usually adopted...ordinary welding temperatures of low-carbon irons. but its effects in these experiments could not be definitely traced. WHAT is LEARNED FROM CHEMICAL... | |
 | Lester Anthony Beardslee - Chains - 1879 - 140 pages
...0.055, 0.033, 0.032, 0.044, 0.068, and including L, 0.351. The weld steel, or steely iron, L (C. 0.35), when treated by the uniform method usually adopted...ordinary welding temperatures of low-carbon irons. but its effects in these experiments could not be definitely traced. WHAT is LEARNED FROM CHEMICAL... | |
 | United States. Board for testing iron, steel and other metals - Metals - 1881 - 804 pages
...Best, С. 0.01Л, 0.002, 0.043, O.OGG, 0.026, ОЛ)32, 0.032, 0.042, 0.055, 0.033, 0.032, 0.0044, 0.68, and, including L, 0.351. The weld-steel, or steely...although it was otherwise a good average chain-iron, with ci medium amount of impurity. Carbon, in a greater degree than phosphorus, promotes fluidity, hence... | |
 | Robert Henry Thurston - Building materials - 1883 - 796 pages
...0.0044, 0.68, and, including A, 0.351. "The weld-steel, or steely-iron, A (C. 0.035), when treated t by the uniform method usually adopted for chain-cable irons, made the worst welds. Iron B, with carbon so low as 0.07, made bad welds, although it was otherwise a good average chain-iron,... | |
 | Robert H. Thurston - Building materials - 1906 - 808 pages
...0.055, °-033, 0.032, 0.0044, O.68, and, including A, 0.351. "The weld-steel, or steely-iron, A (C. 0.035), when treated by the uniform method usually...for chain-cable irons, made the worst welds. Iron B, with carbon so low as 0.07, made bad welds, although it was otherwise a good average chain-iron,... | |
 | Robert Henry Thurston - Building materials - 1909 - 808 pages
...0.055, 0.033, 0.032, 0.0044, 0.68, and, including A, 0.351. "The weld-steel, or steely-iron, A (C. 0.035), when treated by the uniform method usually...for chain-cable irons, made the worst welds. Iron B, with carbon so low as 0.07, made bad welds, although it was otherwise a good average chain-iron,... | |
| |